bm303 Well Established Member

bm303

Posted
Posted
Today I coked my 588 RTG+ DSG wedges, and they came out beautifully. Obviously my objective is to eliminate glare, and I am going to assume that the raw wedge has some glare considering it is much brighter than the rtg finish. Do you recommend that I let the club naturally rust on its own, or should I soak them in salt water overnight? Any help would be great, thanks a ton.
In my bag:
Driver: Tour Burner 10.5 re*ax
3 Wood:R5 XL
Irons:FP Irons 5-GW
Hybrids:Baffler DWS 3,4 Wedges:588 RTG DSG 56º, 60ºPutter:White Hot XG #9 34"Grips: Lamkin Crossline CordsBall: Pro V1x

joshtpa Great Member

joshtpa

Posted
Posted
If you play a couple of times in the morning mist, they will rust within a few days. My Vokeys that I coked sure did.

rebby Great Member

rebby

Posted
Posted
Would somebody mind posting pics of these coked/rusted wedges??? I personally haven't seen one of these yet. Thanks...

Yonex Ezone Type 380 | Tour Edge Exotics CB Pro | Miura 1957 Irons | Yururi Wedges | Scotty Cameron Super Rat | TaylorMade Penta


bm303 Well Established Member

bm303

Posted
  • Author
Posted
Would somebody mind posting pics of these coked/rusted wedges??? I personally haven't seen one of these yet. Thanks...

Pics taken with my iphone, but here you go:

In my bag:
Driver: Tour Burner 10.5 re*ax
3 Wood:R5 XL
Irons:FP Irons 5-GW
Hybrids:Baffler DWS 3,4 Wedges:588 RTG DSG 56º, 60ºPutter:White Hot XG #9 34"Grips: Lamkin Crossline CordsBall: Pro V1x

Magnus Well Established Member

Magnus

Posted
Posted
If they are wet, and exposed to air - they will rust (6th grade chemistry don't fail me now) don't worry about that - it'll happen quick.

In the Titleist bag on the ClicGear 2.0:

PILOT: Titleist 910 D2 Axivore Tour Red

3 WOOD: Callaway 3-Deep 13*

Hybrid: TaylorMade RBZ 22*

IRONS 3-PW: Mizuno MP-32

WEDGES: Vokey TVD 54* SM5 58*K

PUTTER: Rife 2-Bar Blade

BALL: Penta 5


DDBowdoin Great Member

DDBowdoin

Posted
Posted
Today I coked my 588 RTG+ DSG wedges, and they came out beautifully. Obviously my objective is to eliminate glare, and I am going to assume that the raw wedge has some glare considering it is much brighter than the rtg finish. Do you recommend that I let the club naturally rust on its own, or should I soak them in salt water overnight? Any help would be great, thanks a ton.

I wouldn't soak the club... throw salt water into a spray bottle and spray the club

you'll get a lot more rust this way

Daniel Duarte
905R UST Proforce V2 76g 44" S
904F 15, Graphite Design YS6+
MD Hybrid, 19 Degree, UST V2 Hybrid S
Pro M Gunmetal 5-PW, Nippon 1150GH Pro SVokey Oil Can 52 - RAWVokey Spin Milled Oil Can 56, 60 - RAWTEI3 Newport II - Torch Copper- Prov1x


Note: This thread is 6336 days old. We appreciate that you found this thread instead of starting a new one, but if you plan to post here please make sure it's still relevant. If not, please start a new topic. Thank you!

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now
 Share
Go to topic listing


  • Want to join this community?

    We'd love to have you!

    Sign Up

  • TST Partners

    PlayBetter
    Golfer's Journal
    ShotScope
    The Stack System
    FitForGolf
    FlightScope Mevo
    Direct: Mevo, Mevo+, and Pro Package.

    Coupon Codes (save 10-20%): "IACAS" for Mevo/Stack/FitForGolf, "IACASPLUS" for Mevo+/Pro Package, and "THESANDTRAP" for ShotScope. 15% off TourStriker (no code).

  • Posts

    • iacas
      Mizuno Jpx One Driver & Fairway Woods

      By iacas · Posted

      I think you're saying it's preposterous to think that the areas on this club are anything like what's shown here: 30mm toward the toe or heel loses only 5% distance? Highly, highly doubtful. So a guy who hits the ball there and normally hits the ball about 250… will hit it instead about 238. By missing the sweet spot by about 1.2 inches? Highly, highly doubtful. Heck, the high heel barely gets into the red, and orange is only "up to" 10%!
    • 5amZ
      "5 Minutes Daily" Practice Challenge

      By 5amZ · Posted

      Day 151 1-11 flow work today. I've been doing all pause work, so Inwanted to get some rhythm going. Recorded.
    • iacas
      PGA Tour 6 Rule Changes for 2026

      By iacas · Posted

      a) No b) This MLR says: I doubt the MLR is going to affect their weekly league games, in other words.
    • Maroon88
      PGA Tour 6 Rule Changes for 2026

      By Maroon88 · Posted

      So the question was posed today by some of my friends.  Is a pitch mark the same as a divot?  I thought NO, but they argued if your ball lands in another player's divot (made by club during a swing) this was the same as a pitch mark, i.e. the ball mark made when the ball lands  
    • saevel25
      Mizuno Jpx One Driver & Fairway Woods

      By saevel25 · Posted

      Original definition use to or still is how far offline you hit it. It might be better to think of it as consistency in retaining favorable launch conditions to optimize distance.   That heat map showed a gigantic 0-3% loss in ball speed. That is absurd. The true 100% sweet spot is tiny for all clubs. Good luck telling the difference if the sweet spot is under 3% in a sizable area. Especially considering variation in launch angle, spin, and outdoor weather.
×
×
  • Create New...

Important Information

Welcome to TST! Signing up is free, and you'll see fewer ads and can talk with fellow golf enthusiasts! By using TST, you agree to our Terms of Use, our Privacy Policy, and our Guidelines.

  I accept